| Property |
To convert from the
CUSTOMARY UNIT |
multiply by |
RECOMMENDED FORM |
| Bending Stiffness |
gram-force centimetres [gmf-cm] (or Taber units) |
98.0665 |
micronewton meters [µN-m] |
| gram-force centimetres [gmf-cm]
(or Taber units) |
0.0980665 |
millenewton meters [mN-m] |
| pound-force inches [lbf-in] |
0.112985 |
newton meters [N-m] |
| Density |
pounds per cubic foot [lb/ft3] |
16.01846 |
kilograms per cubic meter [kg/m3] |
| grams per cubic centimetre [g/cm3] |
1000 |
kilograms per cubic meter [kg/m3] |
| Edge tearing resistance |
pounds-force [lbf] |
4.44822 |
newtons [N] |
| kilograms-force [kgf] |
9.80665 |
newtons [N] |
| Burst index |
grams force/sq.centimetre/g/m2 |
0.0980665 |
kilopascal squmetres per gram [kPa-m2/g] |
| TEA index |
millijoules per gram [mJ/g] |
1 |
milljoules per gram [mJ/g] |
| Tear index |
100 grams-force per (gram per square meter) [100
gf/(g/m2)] |
0.0980665 |
millinewton sq. meters per grams [mN-m2/g] |
| Tearing strength |
grams-force [gf] |
9.80665 |
millinewtons [mN] |
| Tensile energy absorption (TEA) |
foot pounds-force per square foot [ft-lbf/ft2] |
14.5939 |
joules per square meter [J/m2] |
| inch pounds-force per square
inch [in-lbf/in2] |
175.127 |
joules per square meter [J/m2] |
| kilogram-force meters per square
meter [kgf-m/m2] |
9.80665 |
joules per square meter [J/m2] |
| joules per square meter [J/m2] |
1 |
joules per square meter [J/m2] |
| Tensile index |
kilometres breaking length [km] |
9.80665 |
newton meters per gram [N-m/g] |
| Thickness |
inches [in] |
0.0254 |
millimetre [mm] |